MRL [MRL] Prof. Chong Soo Lee: Effect of grain boundary engineering on hydrogen embrittlement in Fe-Mn-C…
페이지 정보
작성자 최고관리자
댓글 0건 조회 468회 작성일 2019-03-31 19:10
본문
The influence of strain rate (10−3≤ε˙ ≤10−5 s−1) on hydrogen embrittlement behavior of Fe−17Mn−0.8C (wt.%) TWIP steel was investigated. Two types of specimens were tested; one (AR) was hot-rolled, and the other (GBE) was further processed by grain boundary engineering. After hydrogen charging, the fracture strength (FS) and ductility of AR samples decreased as ε˙ decreased, because increasing numbers of H atoms accumulated near crack tips. However, after hydrogen charging, the FS and tensile ductility of GBE samples were not decreased much even at low ε˙ , because special boundaries suppressed hydrogen-induced crack initiation and propagation.
- 이전글[PSL] Prof. Eul-Bum Lee: The Efficacy of the Tolling Model’s Ability to Improve 19.05.14
- 다음글[MML] Prof. F. Barlat: Influence of Yield Stress Determination in Anisotropic Hardening Model on Springback Prediction in Dual-Phase Steel 19.02.28
댓글목록
등록된 댓글이 없습니다.