SSL [SSL]Prof. Sung-Joon Kim: Correlation between grain size variation and hydrogen embrittlement in a c…

페이지 정보

profile_image

작성자 최고관리자

댓글 0건 조회 358회 작성일 2023-08-14 15:37

본문

2921615b3020e0e13258e820d848bbd9_1691995018_7725.jpg
 

Abstract: The effect of grain size variation (11 mm, 34 mm) on the hydrogen-induced tensile properties degradation of a Co-free cost-effective Fe40Mn40Ni10Cr10 austenitic medium entropy alloy was investigated using a slow strain rate test. Despite improving both strength and ductility with decreasing the grain size in non-charged conditions, the fine-grain alloy showed a higher relative elongation loss after electro-chemical hydrogen charging. The larger ductility loss in the fine-grain alloy was ascribed to the fast propagation rate of major intergranular cracks and the drastic strain hardening rate drop of the alloy under hydrogen charging. The Schmid factor analysis showed that the enhanced dislocation activity in the fine-grain alloy compared with coarse-grain one was responsible for rapid hydrogen transfer to the grain boundaries, fast dislocation pile-up behind the grain boundaries, and, consequently, more severe hydrogen embrittlement. The significant stress concentration near the grain boundaries and fast intergranular crack propagation were recognized to be the main reason for premature fracture in fine-grain alloy.

댓글목록

등록된 댓글이 없습니다.